| Photon energy | 1486.61eV |
| Spectrum type | Pd 3p3/2, O 1s |
| Resolution | 20 |
| Lens Mode | ARM22 |
| Dwell Time | 0.1 |
| Step size | 0.1 |
| Number of scans | 5 |
| Name | AgPd in 1 mbar O2 75°C (heating) |
| Ex situ preparation | Quantitative amounts of the Ag (slugs 3×3mm, 99.99%) and Pd (granules <7mm, 99.95%) purchased from EvoChem were melted in a light oven, with a four times re-melting process for homogenization. Afterwards the alloy was cold-rolled to a 1.6 mm thick foil and then annealed for 6h at 800°C for grain size growth. The foil was cut into smaller pieces and polished, with incrementally finer grid, down to a 1 µm using diamond suspension. |
| In situ preparation | cleaned by Ar+ sputter and annealing cycles. After Ar+ sputter cleaning the sample was heated in 0.5 mbar H2 at 450°C for 2 h. For the oxidation experiment the sample was heated in 1 mbar O2 from 70°C-400°C with a ramping speed of 0.3°C/min |
| Measurement Date | 30-09-2020 |
| Condition | Value | Units |
|---|---|---|
| O2 pressure | 1 | mbar |
| Temperature | 75 | °C |
| Analyzer Mode | FAT |
| Area | 0,8 |
| Strength | 180W |
| Source Beam Size | 0,8 |
| Take Off Angle | 90 |
| Analyzer Acceptance Angle | 22 |
| Laboratory | Surface Analytics |
| Instrument | Phoibos NAP-150 |
| Protocol | ISO 15472:2010 |
| Calibration date | 30-09-2020 |
| Binding Energy | 368.18 |
| Emission line | Ag 3d5/2 |